Products < Electric/Electronic materials < Heavy
electric cast molding resins |
 |
| |
|
|
|
| |
|
|
|
 |
| Products
|
Mixng
ratio
(wt%)
|
Viscosity
( at25℃,cps) |
Pot-life
(Pot Life)
|
Cure
condition |
Hardness
(Shore-D)
|
Application |
part A/part
B |
part
A/part B |
|
EML-700
|
100/100
|
35,000/80.000 |
40℃, 10hr |
Curing 80℃x4hr
Post Curing 120℃x7hr |
95
|
Switchgear, Bushing, CT/PT, Bracket |
|
EML-710 |
100/100
|
38,000/70,000
(40℃) |
60℃, 5hr
|
Curing 80℃x4hr
Post Curing 130℃x10hr |
90-95 |
" |
|
EML-720 |
100/80
|
12,000/4,000 |
60℃, 5hr
|
Curing 80℃x4hr
Post Curing 130℃x8hr |
92-95
|
" |
|
EML-730 |
100/100
|
12,000/3,000 |
60℃, 6hr |
Curing 80℃x4hr
Post Curing 130℃x8hr |
80-85 |
CT/PT Bracket
High impact strength |
|
EML-750 |
100/30
|
78,000/80
(40℃/25℃)
|
40℃, 6hr
|
Curing 90℃x3hr
Post Curing 140℃x3hr
|
92 |
Ignition molding |
|
EML-800 |
100/20
|
20,000/150
|
60min(25℃) |
25℃x24hr
|
86-89 |
Room temp. cure, CT/PT |
|
EML-810 |
100/20
|
20,000/150
|
25℃, 60min
|
25℃x24hr
or 50℃x3hr
|
86-89 |
CT/PT (1~5Kg scale)
Flame retardant
|
|
EML-820 |
100/10
|
15,000/600 |
25℃, 45min
|
25℃x23hr
|
86-89 |
Room temp. cure, CT/PT |
|
EML-900 |
100/20
|
380,000/85,000
(40℃)
|
60℃, 5hr |
Curing 80℃x4hr
Post Curing 130℃x8hr |
90-94
|
Out door insulator, CT/PT
Good UV stability
|
|
EML-910 |
100/20
|
130,000/150
(40℃/25℃)
|
60℃, 5hr |
Curing 80℃x4hr
Post Curing 130℃x8hr |
90-94
|
" |
|
EML-920 |
100/20
|
120,000/120
(40℃/25℃) |
60℃, 5hr |
Curing 80℃x4hr
Post Curing 130℃x8hr
|
90-94
|
" |
|
EML-1000 |
100/100
|
250,000/150
(40℃/25℃) |
60℃, 5hr |
Curing 150℃x15min
Post Curing 130℃x10hr
|
90-93 |
Only APG system,
Low shrinkage
|
|
EML-1100 |
100/20
|
230,000/850
(40℃/25℃)
|
60℃, 5hr |
Curing 150℃x15min
Post Curing 130℃x10hr |
70-80
|
In door insulator,
APG system |
|
EML-1200 |
100/20
|
250,000/850
(40℃/25℃) |
60℃, 5hr |
Curing 150℃x15min
Post Curing 130℃x10hr
|
90-93
|
High impact strength
APG system |
|
EML-1300 |
100/20
|
250,000/150
(40℃/25℃) |
60℃, 5hr |
Curing 150℃x15min
Post Curing 130℃x10hr |
90-95 |
High Tg & mechanical properties,
APG system
|
|
EML-2000 |
100/20
|
350,000/70.000
(40℃) |
60℃, 5hr |
Curing 80℃x4hr
Post Curing 130℃x8hr
|
90-95
|
Only used PT |
|
|
High
mechanical properties such as switchgear, Bushing, CT/PT
bracket.